Which part is most essential in aluminum profile extrusion process?

Aluminium profile system has widely applied to machine building, aluminium framework, automation industrial, material handling, belt conveyor system and machine safety guarding,etc. since the materials are Strong, Lightweight, High strength-to-weight ratio, Resilient, Modularity, Easily machined, etc. Now let's talk about the main procedures in the Extrusion works.

production flow.jpg

1. Prepared Extrusion Die 

The dust is machined from H13 steel with a round molded bite. Or on the other hand, if one is accessible from now on, it is pulled out of a distribution center like the one you see here. The pass on must be preheated to between 450-500 degrees celsius before Extrusion to help expand its life and guarantee even metal stream. When the dust is preheated, it can be stacked in the extrusion press.

2. Preheated Aluminum Billet 

Next, a strong, tube-shaped aluminum compound square, called a billet, is cut from a long log of composite material. In a broiler it is preheated to between 400-500 degrees celsius, similar to this one. It makes it robust enough but not liquid for the Extrusion technique.

3.Transferred the Billet to the Extrusion Press

When the billet is preheated it is precisely moved to the Extrusion press. A grease is added to it until it’s stacked into the press. In addition, the discharge specialist is applied to the Extrusion smash, so that the billet and slam do not remain together.

4. Billet Material into the Container

The flexible billet is currently stacked in the Extrusion press, where the slam driven by water applies up to 15,000 tons of strain to it. The billet material is driven into the holder of the extrusion press, as the smash applies pressure.

5. Extrusion rises fit as a fiddle of Die

As the composite material fills the compartment, it is currently being squeezed facing the dust bite of the Extrusion. With continuous weight being added to it, there is no space for the aluminum content to go outside the opening in the bucket jump. It appears from the initial push of the pot, appearing like a complete profile.

6. Extrusions are Guided Along with the Runout Table and Quenched

In the midst of creation, a puller grasps the Extrusion, close to the one you see here, which directs it alongside the runout table at a velocity that schedules its departure from the journal. The profile is “extinguished” as it moves along the runout table, or consistently cooled by a water shower or by fans over the table.

7. Extrusions are Sheared to Table Length

When an Extrusion is at the maximum length of glass, a hot saw can shear it to separate it from the Extrusion process. Temperature carries on a major job during increasing advancement of the process. Although the Extrusion was extinguished after leaving the press, it still hasn’t cooled completely.

8. Extrusions are Cooled to Room Temperature

Table-length Extrusions are precisely moved from the runout table to a cooling table after shearing, similar to the one you see here. Where the profiles must live until they hit room temperature. They should be extended when they do.

9. Extrusions are Moved to the Stretcher and Stretched into Alignment

There has been some frequent curving in the profiles and this will be revised. They are transferred to a cot, to fix this. The profile is grasped precisely on the two finishes and pulled until it is fully straight and taken into the specifics.

10. Extrusions are Moved to the Finish Saw and Cut to Length

They are transferred to the saw table with the table-length Extrusions now straight and fully work-solicited. Here, they are stitched to pre-indicated lengths, mostly in lengths of 8 and 21 feet somewhere. Now, the Extrusions properties coordinate the temper of T4. Upon sawing, they may be transferred to a mature broiler for maturation to the temperature T5 or T6. 

After the review, did you have the concept for the whole process extruded aluminum profile? Welcome to make a note or comment. We'll reply within 12 hours.